Q390钢板； Q390钢板；
Q390，是一种低合金高强度结构钢。
化学成分
【化学成分】（质量分数）（%）
|
等级
|
C
|
Mn
|
Si
|
P
|
S
|
V
|
Nb
|
Ti
|
Al
|
Cr
|
Ni
|
|
A
|
≤0.20
|
1.00～1.60
|
≤0.55
|
≤0.045
|
≤0.045
|
0.02～0.20
|
0.015～0.060
|
0.02～0.20
|
-
|
≤0.30
|
≤0.70
|
|
B
|
≤0.20
|
1.00～1.60
|
≤0.55
|
≤0.040
|
≤0.040
|
0.02～0.20
|
0.015～0.060
|
0.02～0.20
|
-
|
≤0.30
|
≤0.70
|
|
C
|
≤0.20
|
1.00～1.60
|
≤0.55
|
≤0.035
|
≤0.035
|
0.02～0.20
|
0.015～0.060
|
0.02～0.20
|
≥0.015
|
≤0.30
|
≤0.70
|
|
D
|
≤0.20
|
1.00～1.60
|
≤0.55
|
≤0.030
|
≤0.030
|
0.02～0.20
|
0.015～0.060
|
0.02～0.20
|
≥0.015
|
≤0.30
|
≤0.70
|
|
E
|
≤0.20
|
1.00～1.60
|
≤0.55
|
≤0.025
|
≤0.025
|
0.02～0.20
|
0.015～0.060
|
0.02～0.20
|
≥0.015
|
≤0.30
|
≤0.70
|
力学性能
【抗拉强度】（σb/MPa）
490～650
【伸长率】（δ5/%）
|
等级
|
δ5/%
|
|
A
|
≥19
|
|
B
|
≥19
|
|
C
|
≥20
|
|
D
|
≥20
|
|
E
|
≥20
|
【屈服点】（σs/MPa）
|
厚度（直径、边长）/mm
|
≤16
|
>16～35
|
>35～50
|
>50～100
|
|
σs/MPa
|
≥390
|
≥370
|
≥350
|
≥330
|
【冲击吸收功】（Akv（纵向）/J）
|
等级￤温度
|
+20℃
|
0℃
|
-20℃
|
-40℃
|
|
A
|
|
|
|
|
|
B
|
≥34
|
|
|
|
|
C
|
|
≥34
|
|
|
|
D
|
|
|
≥34
|
|
|
E
|
|
|
|
≥27
|
主要特性
综合力学性能好，焊接性、冷、热加工性能和耐蚀性能均好，C、D、E级钢具有良好的低温韧性。
应用举例
船舶、锅炉、压力容器、石油储罐、桥梁、电站设备、起重运输机械及其他较高载荷的焊接结构件。