碳纤维PEEK LNP Thermocomp LC-1006
PEEK 基础创新塑料(美国) LC-1006
LNP Thermocomp® LC-1006 Polyetheretherketone,
Carbon Fiber Reinforcement
Polymer,Thermoplastic,Polyketone,Polyetheretherketone (PEEK),Polyetheretherketone, PEEK, Carbon Fiber Filled
碳纤维30%填充聚醚醚酮PEEK
LNP Thermocomp® LC-1006 Polyetheretherketone, Carbon Fiber Reinforcement 物性表
|
物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
|
|
比重 |
1.41 g/cc |
1.41 g/cc |
Method A; ASTM D792 |
|
|
线性成型收缩率 |
0.0010 cm/cm |
0.0010 in/in |
ASTM D955 |
|
|
线性成型收缩率，横向 |
0.0040 cm/cm |
0.0040 in/in |
ASTM D955 |
|
|
热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
|
|
线性热膨胀系数 |
11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
|
|
线性热膨胀系数,横向流动 |
29.0 µm/m-°C @Temperature 20.0 °C |
16.1 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
|
|
载荷下热变形温度(0.46 MPa) |
299 °C |
570 °F |
Unannealed; ASTM D648 |
|
|
载荷下热变形温度(1.8 MPa) |
299 °C |
570 °F |
Unannealed; ASTM D648 |
|
|
可燃性(UL94) |
V-0 @Thickness 0.770 mm |
V-0
@Thickness 0.0303 in |
|
|
|
加工性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
|
|
加工（熔体）温度 |
379 - 388 °C |
714 - 730 °F |
|
|
|
模具温度 |
135 - 163 °C |
275 - 325 °F |
|
|
|
干燥温度 |
121 - 149 °C |
250 - 300 °F |
|
|
|
干燥时间 |
4 hour |
4 hour |
|
|
|
水分含量 |
0.10 % |
0.10 % |
Suggested |
|
|
背压 |
0.345 - 0.689 MPa |
50.0 - 99.9 psi |
||