| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D-792 | 1.36 | |||
| 吸水率 | 23℃·24小时 | ASTM D-570 | 0.07 | % | ||
| 膜塑收缩 | 80×80×3板材 | 0.6-1.5 | % | |||
| 机械性能 | 断裂拉伸伸长 | 23℃ | ASTM D-638 | 5 | % | |
| 磨擦系数 | 金属 | ASTM D-1894 | 0.14 | |||
| 本身 | ASTM D-1894 | 0.19 | ||||
| 弯曲模量 | 23℃ | ASTM D-790 | 48 | kg/cm2×103 | ||
| 泰伯磨耗量 | 1.000g·CS-17轮 | ASTM D-1044 | 18 | 毫克/1.000m | ||
| 负荷下的 | 4.6kg/cm | ASTM D-648 | 220 | ℃ | ||
| 18.6kg.cm | ASTM D-648 | 204 | ℃ | |||
| IZOD冲击强度(1/8时宽) | 无缺口 | 23℃ | ASTM D-256 | 60 | kg·cm/cm | |
| 无缺口 | -40℃ | ASTM D-256 | 40 | kg·cm/cm | ||
| 缺口 | 23℃ | ASTM D-256 | 13.5 | kg·cm/cm | ||
| 缺口 | -40℃ | ASTM D-256 | 10.0 | kg·cm/cm | ||
| 弯曲强度 | 23℃ | ASTM D-790 | 1300 | kg/cm2 | ||
| 拉伸强度 | 23℃ | ASTM D-638 | 900 | kg/cm2 | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 89 | M标度 | ||
| 压缩强度 | 23℃ | ASTM D-695 | 930 | kg/cm2 | ||
| 电气性能 | 介电强度 | 短时·23℃·1/8时 | ASTM D-149 | 22(18) | KV/mm | |
| 抗电弧性 | ASTM D-495 | 110 | 秒 | |||
| 体积电阻率 | ASTM D-257 | 2.0(0.8) | cm/cm×1016 | |||
| 热性能 | 线性热膨胀 | ASTM D-696 | 5.5 | cm/cm℃×105 | ||