③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | >0.01 | % | |
| 熔体流动速率 | ASTM D-1238 | 19 | g/10min | ||
| 密度 | ASTM D-792 | 0.90 | g/cm3 | ||
| 机械性能 | 拉伸强度 | ASTM D-638 | 310 | kgf/cm2 | |
| 冲击强度 | 带缺口 | ASTM D-256 | 7 | kgf.cm/cm | |
| 弯曲模量 | ASTM D-790 | 11000 | kgf/cm2 | ||
| 线型成型收缩率 | KPIC Method | 1.0-2.0 | % | ||
| 洛氏硬度 | ASTM D-785 | 90 | scRale | ||
| 绝缘强度 | ASTM D-149 | 40 | KV/mm | ||
| 断裂伸张率 | ASTM D-638 | <500 | % | ||
| 电气性能 | 耐电弧性 | ASTM D-495 | 130 | sec. | |
| 介电常数 | ASTM D-150 | 2.3 | |||
| 损耗因素 | ASTM D-150 | 2 | 10-4 | ||
| 体积电阻率 | ASTM D-257 | 1 | 1017ohm.cm | ||
| 热性能 | 熔点 | ASTM D-3418 | 148 | ℃ | |
| 比热容 | KPIC Method | 0.46 | cal/g℃ | ||
| 传热系数 | KPIC Method | 3 | 10-4calcm/cmsec,℃ | ||
| 热变形温度 | ASTM D-648 | 90 | ℃ | ||